It was reported by a healthcare professional in china that during an elbow procedure on (b)(6) 2023, it was observed that the anchor on the lupine loop rapide anchor w/orthocord ds device was deformed upon opening its package.During in-house engineering evaluation, it was determined that the anchor was bent near mid-body.Another device was used to complete the surgery.There were no adverse consequences to the patient.No additional information could be provided.
|
This report is being submitted in pursuant to the provisions of 21 cfr, part 803.This report may be based on information which has not been able to investigate or verify prior to the required reporting date.This report does not reflect a conclusion by depuy mitek or its employees that the report constitutes an admission that the device, depuy mitek, or its employees caused or contributed to the potential event described in this report.If information is obtained that was not available for the initial medwatch, a follow-up medwatch will be filed as appropriate.Device was used for treatment, not diagnosis.If information is obtained that was not available for the initial medwatch, a follow-up medwatch will be filed as appropriate.H10 additional narrative: udi: (b)(4).Investigation summary: both photo and the complaint device were received and evaluated.A photo was returned to depuy synthes mitek for evaluation.The depuy synthes mitek team conducted a visual inspection of the returned photo.Visual analysis of the photo revealed that the device was shown over its outer packaging, it was observed that the anchor was bent, also it was noted that the suture was completely out of the device, the shaft appeared to be in a normal condition.According with the visual inspection of the photo, this complaint can be confirmed.Hands on analysis should provide the required evidence to provide a root cause.The product was returned to mitek for evaluation.Mitek then conducted visual inspection of device received.Upon visual inspection, it was observed that the anchor was bent near mid-body, confirming this complaint.A partial part of the suture shows foreign matter, presumably biological matter.A manufacturing record evaluation was performed for the finished device lot number: 9l60576, and no non-conformances were identified.No further information regarding the cause of the defect has been provided to help determine a root cause for this failure.If the component (poly (lactide[1]coglycolide) polymer and tricalcium phosphate (tcp)) of this device is exposed to high temperatures, its structure gets compromised as it tents to lose mass, it provides flexibility to the polymer chains producing a decrease in the degree of crystallinity of the structure and the microhardness values causing these types of deformations.These conditions have typical characteristics of material exposed to temperatures higher, however this cannot be conclusively determined.Based on the results, the probable root cause of this failure is that the devices were exposed to an elevated temperature before it was opened in the operating room prior to surgery.An investigation with r&d was performed for further investigation; a possible root cause for this condition could be a combination of the elevated temperature and the slight tension on the suture could result in the bending of the anchor.Per further analysis, the risk level for visual: deformed/bent is an acceptable risk (ar) within risk management documents.Per ifu-109002, lupine br anchor system, ¿storage¿ section to store in a ¿cool and dry¿ place.As part of mitek¿s quality process all devices are manufactured, inspected, and released to approved specifications.At this point in time, no corrective action is required, and no further action is warranted.However, depuy synthes mitek will continue to track any related complaints within this device family as a means of monitoring the extent with which this complaint is observed in the field.
|