SMITH & NEPHEW, INC. REDAPT STEM EXTRACTOR UNIV JOINT; PROSTHESIS,HIP,SEMICONSTRAINED,METALCERAMIC/POLYMER, CEMENTED OR NON-POROUS
|
Back to Search Results |
|
Model Number 71355107 |
Device Problem
Crack (1135)
|
Patient Problem
No Clinical Signs, Symptoms or Conditions (4582)
|
Event Date 12/20/2021 |
Event Type
malfunction
|
Event Description
|
It was reported that when extracting the stem during thr surgery, the green plastic piece of a redapt stem extractor univ joint cracked outside the patient.Surgery was resumed, without any delay, with the same device.Patient was not harmed as consequence of this problem.
|
|
Manufacturer Narrative
|
(b)(4).
|
|
Manufacturer Narrative
|
H3, h6: the associated device was returned and evaluated.A visual inspection of the device was conducted and confirmed the device is cracked in the middle, rendering it inoperative.The device exhibits signs of significant wear and use.A review of complaint history revealed similar events for the listed device, but no similar events for the batch, this failure mode will be monitored for future complaints for any necessary corrective actions.A review of the manufacturing records did not reveal a manufacturing abnormality that could have caused or contributed to the reported incident.At this time, we do not have reason to suspect that the product failed to meet any product specifications at the time of manufacture.A review of the risk management file revealed this failure mode was previously identified.The anticipated risk level is still adequate.Assessment of historical escalated cases concluded that there are no prior actions related to this device and failure mode.A contribution of the device to the reported event could be corroborated as the device shows signs of damage/wear.This device is a reusable instrument that can be exposed to numerous surgeries.Damage from prolonged use, misuse or rough handling are probable causes of the reported event.We recommend that all reusable instruments be routinely inspected for wear and damage and replaced as necessary.Based on this investigation, the need for corrective action is not indicated.Should additional information be received, the complaint will be reopened.No further investigation is warranted for this complaint; however, we will continue to monitor future complaints and investigate as necessary.We consider this investigation closed.
|
|
Manufacturer Narrative
|
H3, h6: the device was not returned for evaluation and the reported event could not be confirmed.The contribution of the device to the reported event could not be corroborated.A review of the manufacturing records did not reveal a manufacturing abnormality that could have caused or contributed to the reported incident.A review of complaint history revealed similar events for the listed device, but no similar events for the batch, this failure mode will be monitored for future complaints for any necessary corrective actions.A review of the risk management file revealed this failure mode was previously identified.The anticipated risk level is still adequate.A historical review concluded that there are no prior actions related to this product and event.At this time, we have no reason to suspect that the product failed to meet any product specifications at the time of manufacture.This device is a reusable instrument that can be exposed to numerous surgeries.Damage from prolonged use, misuse or rough handling are likely probable causes of the reported event.We recommend that all reusable instruments be routinely inspected for wear and damage and replaced as necessary.Based on this investigation, the need for corrective action is not indicated.Without the return of the actual product involved, our investigation could not proceed.Should the device or additional information be received, the complaint will be reopened.No further investigation is warranted for this complaint; however, we will continue to monitor for future complaints and investigate as necessary.We consider this investigation closed.
|
|