(b)(4).Date sent: 9/17/2026.D4 batch#: a99k5g.Investigation summary:
the product was returned for evaluation.Visual inspection and functional testing were conducted on the returned device.The device was returned with the distal tip of the blade broken off and not returned.The remaining blade portion was scratched, with evidence of contact with metal in or out of the operative field.During functional testing on energy systems, an alert screen was displayed.A probable cause for the device to stop activating and the energy systems to display an alert screen is blade damage.The device was disassembled to verify the internal components, and no anomalies were found.Probable causes of blade damage, including breakage, are external contact during pre-op or general use, blade contact with other devices, staples or clips during the procedure, or using any means other than the blade wrench to attach or detach the blade.Once minor blade damage has occurred, subsequent activations may increase the severity of the blade damage.This in turn can result in activation issues such as failing the pre-run test with the generator and displaying an alert screen.These alert screens that can result are such as ¿blade error detected¿ or "relaxed pressure on blade" followed by a ¿replace instrument¿ screen later in the procedure.Continued usage of the damaged blade can result in a broken blade.As part of ees quality process all devices are manufactured, inspected, and released to approved specifications.A manufacturing record evaluation was performed for the finished device lot/batch a99k5g, and no non-conformances were identified.
|